Single crystal growth, structural characteristics and magnetic properties of chromium substituted M-type ferrites

• Growth of large crystals of Cr substituted (Ba,Sr)Fe12O19 from two different fluxes.
• Cr-substitution in a large range of compositions.
• Cr/Fe order revealed by Mößbauer spectroscopy.
• All Cr and Fe in oxidation state +3 present.
• Anisotropic magnetic properties determined.

Two different types of fluxes, namely sodium based and chloride based fluxes were used to grow Cr substituted barium and strontium hexaferrite ferrite crystals, (Sr,Ba)Fe12 − xCrxO19 at comparatively low temperatures of about 1300 °C. The sodium based flux led to growth of larger crystals up to 5 mm, but with only minor Cr contents x ≤ 0.07. From the chloride based flux the obtained Cr contents are significantly higher with x = 5.7 (Sr) and x = 3.4 (Ba), however, crystals reach only sizes in the sub-mm range. X-ray absorption spectroscopy data support exclusively isovalent substitution of Fe3+ by Cr3+ even for very low Cr contents. 57Fe Mößbauer spectroscopy reveals Cr to preferentially occupy the six-fold by oxygen coordinated site at 12k and, to a lower degree, 2a and 4f2 in space group P63/mmc. All characteristic magnetic properties drop upon Cr substitution, e. g., the Curie temperature from 728 K for pure BaFe12O19 to 465 K for BaFe8.6Cr3.4O19, the saturation magnetization from 71 emu/g to 29.7 emu/g and the coercive field from 363 Oe to 45 Oe.

Figure optionsDownload as PowerPoint slide