The influence of laser wavelength and fluence on palladium nanoparticles produced by pulsed laser ablation in deionized water

• Palladium nanoparticles were synthesized via liquid laser ablation.
• Size and morphology of nanoparticles depends on the laser wavelength and fluence.
• Lower wavelength and fluence resulted in nanoparticles with smaller sizes (3–6 nm).
• Absorption edge shifts towards longer wavelength with respect of laser wavelengths.

Homogeneous spherical palladium (Pd) nanoparticles were synthesized by pulsed laser ablation of a solid Pd foil target submerged in deionized water, without the addition of any external chemical surfactant. The influence of laser wavelength (355, 532, and 1064 nm) and fluence (8.92, 12.74, and 19.90 J/cm2) on nucleation, growth, and aggregation of Pd nanoparticles were systematically studied. Microstructural and optical properties of the obtained nanoparticles were studied by field emission transmission electron microscopy (FETEM), energy dispersive X-ray spectroscopy, and UV–vis spectroscopy. FETEM micrographs indicate that the average nanocrystallite sizes are relatively low (3–6 nm) and homogeneous for the particles synthesized at the laser wavelengths of 355 and 532 nm. However, at a laser wavelength of 1064 nm, the average nanocrystallite size is relatively large and inhomogeneous in nature. Moreover, we observe that the mean diameter and production rate of particles increases with an increase in laser fluence. The selected area electron diffraction patterns obtained from isolated Pd nanoparticles show the characteristic diffused electron diffraction rings of polycrystalline materials with a face-centered cubic structure. Absorbance spectrum of the synthesized nanoparticle solution shows a broad absorption band, which corresponds to a typical inter-band transition of a metallic system, indicating the production of pure palladium nanoparticles. The present work provides new insights into the effect of laser wavelength and fluence on the control of size and aggregation of palladium nanoparticles in the liquid medium.

Figure optionsDownload as PowerPoint slide