Synthesis and thermoelectric properties of the (GeTe)1-x(PbTe)x alloys

The Ge-rich (GeTe)1-x(PbTe)x alloys with x = 0.10, 0.14, 0.18 and 0.22 were prepared by induction melting, ball milling and spark plasma sintering techniques. The thermoelectric properties of the samples were investigated. The experimental results show that all samples consist of the solid solutions of the two phases GeTe and PbTe. The samples are of p-type semiconductors. The existence of PbTe solution in GeTe increases its resistivity and Seebeck coefficient slightly, but reduces its thermal conductivity significantly. As result, the figures of merit for the materials can be enhanced. The maximum figure of merit ZT value of 0.81 was obtained in the sample (GeTe)0.82(PbTe)0.18 at 673K.