A phase transition from the cubic CsCl-type structure (Pm-3m space group) into a tetragonal UPb-type structure (I41/amd) is observed for the LiAg binary compound at ambient conditions. The crystal structure of the tetragonal modification of the LiAg binary compound was solved by direct methods in SHELXS on the base of structure factors which were extracted from a powder diffraction pattern and refined by SHELXL and the Rietveld method (a = 3.9605(1), c = 8.2825(2) Å, Bragg R-factor = 4.81, Rf-factor = 4.87). Elevated temperatures and/or a small Li-excess versus the equimolar composition favour the cubic structure whereas ambient and lower temperatures and/or a small Li-deficiency stabilize the tetragonal structure. This reconstructive transition is reversible but proceeds slowly.
Figure optionsDownload as PowerPoint slide
Journal: Solid State Sciences - Volume 12, Issue 2, February 2010, Pages 274–280