Phase transitions of CaTiO3 ceramics sintered with the aid of NaF and MgF2

New phases with initial composition (1 − x)CaTiO3 − xNaF − xMgF2 (0 ≤ x ≤ 0.20) have been prepared at low temperature (950 °C) from mixtures of CaTiO3 and fluorides NaF and MgF2. The oxyfluorides obtained have been characterized by X-ray diffraction at room temperature and indexed by isotypy with orthorhombic CaTiO3. The microstructures of these phases are observed by scanning electron microscopy. Dielectric measurements have been carried out during cooling cycle from 500 °C to room temperature at two frequencies (100 Hz, 1 kHz). Differential scanning calorimetry (DSC), thermogravimetry (TG) and differential thermogravimetry (DTG) analyses have been performed, respectively, from room temperature up to 550 °C (DSC) and 920 °C (TG–DTG). The dielectric measurements revealed two anomalies which have been confirmed by DSC analyses. These phenomena are ascribed to second order phase transitions. The variation of the real permittivity with temperature is in agreement with the class I capacitor specifications. However, the dielectric losses have to be improved.

Figure optionsDownload as PowerPoint slide