Thermoelectric properties of LaCo1−xNixO3 polycrystalline samples and epitaxial thin films

Epitaxial thin films of LaCo1−xNixO3 were deposited on MgO (100) substrates by pulsed reactive crossed-beam laser ablation (PRCLA). The electrical transport and thermopower of the epitaxial La(Co,Ni)O3 thin films were measured in a broad temperature range and their thermoelectric activity was compared with bulk samples. The measured films show positive Seebeck coefficient values indicative of p-type conduction. The thin films display a better thermoelectric performance at high temperatures compared to the polycrystalline samples.

The electrical transport and thermopower of epitaxial La(Co,Ni)O3 thin films have beenmeasured in a broad temperature range and their thermoelectric activity has been comparedto bulk samples.Figure optionsDownload as PowerPoint slide