Preparation and characterization of ZnS/CdS bi-layer for CdTe solar cell application

• Synthesizing ZnS/CdS bilayer.
• Improving optical property of window layer.
• Improving CdTe solar cell performance with annealed ZnS/CdS window layer.
• Fabricating homogeneous CdTe solar cell with ZnS/CdS bilayer.

In this work, bilayer ZnS/CdS film was prepared as an improved window layer of CdTe solar cell. TEM was used to observe the cross section of the bilayer structure. The total thickness of ZnS/CdS film was about 60 nm, which could allow more photons to pass through it and contribute to the photocurrent. Optical properties of the bilayers were investigated using UV–vis spectroscopy. Compared with poor transmission of standard CdS film in the short wavelength range of 350–550 nm, the transmission of ZnS/CdS was improved and reached above 50%. The ZnS/CdS was annealed with CdCl2. X-ray photoelectron spectroscopy (XPS) was used to investigate its chemical properties. A possible diffusion between CdS and ZnS was observed after annealing. The efficiency of standard CdS/CdTe solar cell was 9.53%. The device based on ZnS/CdS window layer had a poor 6% efficiency. With annealing treatment on ZnS/CdS layer, the performance was improved and reached 10.3%. In addition, the homogeneity of solar cell performance was improved using ZnS/CdS window layer. A thin ZnS layer was quite effective to reduce the possible shunt paths and short parts of window layer and consequently contributed to fabrication of a homogeneous CdTe solar cell.

Performances and uniformity of CdTe solar cells are improved with new window layer (annealed ZnS/CdS bilayer).Figure optionsDownload as PowerPoint slide