Intercalation of lithium ions into bulk and powder highly oriented pyrolytic graphite

The electrochemical reactions of highly oriented pyrolytic graphite (HOPG) bulk and powder electrodes in 1 M LiPF6 1:1 EC/DMC solution were investigated and the results show that the intercalation reaction of lithium ion into HOPG electrode occurs only at the edge plane and SEI formation reaction on the basal plane is negligible in comparison with that on the edge plane. The active surface area of HOPG powder electrode could be deduced by comparing the peak area (consumed charge for SEI formation) at potential of 0.5 V on voltammograms with that of bulk HOPG edge electrode. The diffusion coefficients of lithium ion in HOPG bulk layers and in HOPG powder was for the first time measured by use of electrochemical impedance spectra and potential step chronamperameter methods. It was found that the diffusion coefficients of lithium in HOPG were in the range of 10−11–10−12 cm2 s−1 for the lithium–HOPG intercalation compounds at potentials from 0.2 (vs. Li/Li+) to 0.02 V, decreasing with the increase of lithium intercalation degree. A good agreement was obtained between the results from bulk and powder HOPG electrodes by electrochemical impedance spectra method.