![عکس صفحه اول مقاله: Synthesis, characterization and catalytic activity studies of Pd-based supported nanoparticle catalyst anchoring on poly(N-vinyl-2-pyrrolidone) modified CMK-3 Synthesis, characterization and catalytic activity studies of Pd-based supported nanoparticle catalyst anchoring on poly(N-vinyl-2-pyrrolidone) modified CMK-3](/preview/png/1523551.png)
Pd nanoparticle-poly(N-vinyl-2-pyrrolidone)/CMK-3 (Pd-PVP/CMK-3) composite was prepared by in situ polymerization method which was effectively employed as a novel heterogeneous catalyst for the Suzuki–Miyaura cross-coupling reaction. The physical and chemical properties of Pd nanoparticle-PVP/CMK-3 were investigated using FT-IR, XRD, BET, UV–vis, TEM and TGA techniques. The reaction was carried out between aryl halides and phenylboronic acid in the presence of water at room temperature. The stability of the catalyst was good and could be reused 10 times without much loss of activity in Suzuki–Miyaura reaction.
Figure optionsDownload as PowerPoint slideHighlights
► A hybrid catalyst was prepared based on a carbon mesoporous material.
► The catalyst showed excellent activity for Suzuki–Miyaura reaction in water.
► The stability of the catalyst was excellent and could be reused 10 times.
► The catalytic activity of Pd-PVP/CMK-3 was compared with Pd-PVP/SBA-15.
► In comparison to Pd-PVP/SBA-15, Pd-PVP/CMK-3 showed higher activity at shorter time.
Journal: Materials Chemistry and Physics - Volume 130, Issue 3, 1 November 2011, Pages 1287–1293