Fabrication of zeolite L thin films with different orientations using anisotropic growth of seed crystals by secondary growth method
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد مواد الکترونیکی، نوری و مغناطیسی
پیش نمایش صفحه اول مقاله
Fabrication of zeolite L thin films with different orientations using anisotropic growth of seed crystals by secondary growth method
چکیده انگلیسی

Zeolite L thin films were fabricated by applying fine zeolite L seed crystals on glass substrates and then hydrothermally treating the seeded substrates in reaction sols. The influence of anisotropic growth of the seed crystals on the orientation of the films was examined. The reaction sols were prepared by mixing KOH, Al, colloidal silica, and water. With increasing the amount of the KOH in the sols or with decreasing the hydrothermal temperature, the zeolite L crystals obtained from the sols changed from a rod-like shape to a clam-like one, indicating a decrease in the relative rate of the growth along the c-axis of zeolite L with a hexagonal lattice to one normal to the c-axis. For the film fabricated at a small amount of KOH or at a high hydrothermal temperature, the c-axis of the zeolite crystals was oriented normal to the substrate. The fabrication at a large amount of KOH or at a low hydrothermal temperature led to films consisting of zeolite crystals whose c-axis is parallel to the substrate. When the aspect ratio of the precipitated crystals decreased to about one, the c-axis of the zeolite crystals in the films became parallel to the substrate.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Chemistry and Physics - Volume 109, Issues 2–3, 15 June 2008, Pages 347–351