![عکس صفحه اول مقاله: Effect of alloying elements on interface microstructure of Mg–Al–Zn magnesium alloys and titanium joint by friction stir welding Effect of alloying elements on interface microstructure of Mg–Al–Zn magnesium alloys and titanium joint by friction stir welding](/preview/png/1530803.png)
An effect of alloying element on interfacial microstructure of Mg–Al–Zn alloys and Ti dissimilar butt joints by friction stir welding (FSW) was studied. Mg–Al–Zn alloy and Ti plates of 2 mm in thickness were successfully butt joined by inserting a probe into the Mg alloy plate and slightly offsetting it by 0.5 mm into the Ti plate side. Al-rich thin layers and Ti–Al intermetallic compound layers formed at the interface of these joints. The thickness of the intermetallic compound layer increased with increasing aluminum content of the Mg–Al–Zn alloy. The tensile strength of the joint decreased with increasing aluminum content. A fracture occurred near the joint interface in a tensile test. This suggests that the thickness of the Ti–Al intermetallic compound layer affected the tensile strength of the joints.
Journal: Materials Science and Engineering: B - Volume 161, Issues 1–3, 15 April 2009, Pages 46–49