![عکس صفحه اول مقاله: Electroluminescent efficiency of alternating current thick film devices using ZnS:Cu,Cl phosphor Electroluminescent efficiency of alternating current thick film devices using ZnS:Cu,Cl phosphor](/preview/png/1531928.png)
ZnS:Cu,Cl phosphor is prepared with the help of low intensity milling of the precursor material in two step firing process. The synthesized phosphor is used for the preparation of alternating current thick film electroluminescent (ACTFEL) devices with screen-printing method. The commission international de l’Eclairge (CIE) color co-ordinates of the ACTFEL devices prepared by these phosphor layers shows a shift from bluish-green to green region with the change in the amount of Cu in the phosphor. The various parameters to improve the efficiency and luminance of the devices have also been investigated. The brightness of the ac thick film EL device depends on the particle size of the phosphor, crystallinity, amount of binding material and applied voltage. The EL device fabricated with phosphor having average particle size of 25 μm shows maximum luminescence, when 60% phosphor concentration is used with respect to binding material. EL intensity is also linearly dependent on frequency. It is due the increase of excitation chances of the host matrix or dopant ions with increasing frequency.
Journal: Materials Science and Engineering: B - Volume 131, Issues 1–3, 15 July 2006, Pages 271–276