Germanium (Ge) and silicon nanocrystals (NCs) are synthesized by one step Ge ion implantation into thermally grown SiO2 layers and subsequent annealing. X-ray diffraction and Raman scattering studies on implanted samples reveal that Ge nanocrystals of sizes 4–13 nm are formed embedded in SiO2 for Ge fluence in the range 3 × 1016 to 2 × 1017 cm−2. At high fluence (≥1 × 1017 cm−2) and annealing temperature of 950 °C, in addition to these Ge NCs, Si NCs are formed at the interface between Si and SiO2 layer as a result of ion impact. Optical Raman spectra show a distinct peak at ∼503 cm−1 corresponding to the Si NCs. The average size of the Si NCs are smaller than the average size of the Ge NCs. Implications of our results are discussed in the light of the versatility of the ion-beam technique for the synthesis of varieties of embedded NCs.
Journal: Materials Science and Engineering: B - Volume 128, Issues 1–3, 15 March 2006, Pages 201–204