Ball Milling Synthesis and Property of Nd0.7Sr0.3MnO3 Manganites

Strontium doped perovskite-type Nd0.7Sr0.3MnO3 ceramics were synthesized completely by high-energy ball milling raw oxides of Nd2O3, SrCO3 and MnO2. The optimal ball milling time and mass ratio of milling balls to raw materials are 4 h and 10:1, respectively. The grain size of as-milled Nd0.7Sr0.3MnO3 ceramics ranges from 51 to 93 nm, and the fine particles contain two phases of crystalline phase and amorphous phase. For the Nd0.7Sr0.3MnO3 synthesized by ball milling and sequent heat treatment, a remarkable colossal electroresistance (CER) effect is observed and the CER ratio reaches 900% at Curie temperature TC when the load voltage increases from 0.1 to 0.8 V.