![عکس صفحه اول مقاله: Improvement of CO2 adsorption on ZIF-8 crystals modified by enhancing basicity of surface Improvement of CO2 adsorption on ZIF-8 crystals modified by enhancing basicity of surface](/preview/png/156271.png)
The imidazolate framework ZIF-8 samples were modified separately by using ammonia impregnation and thermal treatment in atmosphere of N2 or H2 in order to improve its adsorption property toward CO2, and the modified samples A-ZIF-8, N-ZIF-8 and H-ZIF-8 were correspondingly available. The modified ZIF-8 samples were characterized, and the surface chemical properties of the ZIF-8 samples were determined separately by FTIR, CO2-TPD, NH3-TPD and H2O-TPD. The isotherms of CO2 on the modified ZIF-8 samples were measured. Results showed that after surface modification, the total amounts of basicity of the modified samples significantly increased, and followed the order: A-ZIF-8>H-ZIF-8>N-ZIF-8>O-ZIF-8. The uptakes of CO2 increased proportionally with the basic groups on the surfaces of the ZIF-8 samples due to CO2 being an acidic molecule. As a consequence of that, the CO2 adsorption capacity of the samples followed the order: A-ZIF-8>H-ZIF-8>N-ZIF-8>O-ZIF-8. The amount adsorbed of CO2 on the modified ZIF-8 sample by ammonia impregnation is the highest, having an increase.
► ZIF-8 was modified by ammonia impregnation and thermal treatment in gaseous N2 or H2.
► Ammonia impregnation has the CO2 uptake of modified ZIF-8 increase by 45%.
► The CO2/N2 selectivity of modified ZIF-8 has a maximum increase of 56%.
► The hydrophobility of modified ZIF-8 was improved due to increase of surface basicity.
Journal: Chemical Engineering Science - Volume 66, Issue 20, 15 October 2011, Pages 4878–4888