عنوان انگلیسی مقاله ISI
Luminescence properties of MgO: Fe3+ nanopowders for WLEDs under NUV excitation prepared via propellant combustion route
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Luminescence properties of MgO: Fe3+ nanopowders for WLEDs under NUV excitation prepared via propellant combustion route Luminescence properties of MgO: Fe3+ nanopowders for WLEDs under NUV excitation prepared via propellant combustion route](/preview/png/1570461.png)
چکیده انگلیسی
Nanoparticles of Fe3+ doped (0-9 mol %) MgO were prepared using low temperature (400 °C) solution combustion technique using glycine as fuel. The powder X-ray diffraction (PXRD) patterns of the as-formed product exhibit cubic phase without further calcination. The effect of Fe3+ ions on luminescence properties of MgO was studied and results were discussed in detail. The phosphors exhibit strong red emission upon 378 nm (6A1(6S) â 4E(4G)) excitation. The characteristic photoluminescence (PL) peaks recorded at â¼513, 618 and 720 nm were attributed to transition of 4E + 4A1 (4G)â6A1 (6S), 4T2 (4G)â6A1 (6S), 4T1 (4G)â6A1 (6S) respectively. Further, the sample exhibit strong red emission at 720 nm, as a result the phosphor was useful for the applications for (NUV) excitation. The intensity of red emission was attributed to intrinsic defects, especially oxygen-vacancies, which could assist the energy transfer from the MgO host to the Fe3+ ions. The Commission International De I-Eclairage chromaticity co-ordinates were calculated from emission spectra and the values (x,y) were very close to National Television System Committee standard value of white emission. Therefore, the present phosphor was highly useful for display applications.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Radiation Research and Applied Sciences - Volume 8, Issue 3, July 2015, Pages 362-373
Journal: Journal of Radiation Research and Applied Sciences - Volume 8, Issue 3, July 2015, Pages 362-373
نویسندگان
P.B. Devaraja, D.N. Avadhani, H. Nagabhushana, S.C. Prashantha, S.C. Sharma, B.M. Nagabhushana, H.P. Nagaswarupa, B. Daruka Prasad,