• In-situ characterization of γ/α transformation
• EBSD characterization of γ/α transformation orientation relationship
• Extent of interphase precipitation can be controlled through controlled cooling
In-situ characterization techniques have been applied to elucidate the influence of γ/α transformation upon the extent of interphase precipitation in a low-carbon, vanadium-HSLA steel. Electron Back-scattered diffraction analyses of the γ/α orientation relationship with continuous cooling at 2 and 10 K/s suggest that the proportion of ferrite likely to hold interphase precipitation varies little with cooling rate. However, TEM analyses show that the interphase precipitation refines with increasing cooling rate in this cooling range. With cooling rates in excess of 20 K/s, interphase precipitation is increasingly suppressed due to the increasingly diffusional-displacive nature of the Widmanstätten γ/α transformation that is activated. The present study illustrates that the extent and dimensions of interphase precipitation can be controlled through controlled cooling.
Journal: Materials Characterization - Volume 115, May 2016, Pages 83–89