Effect of cold drawing ratio on γ′ precipitation in Inconel X-750

• The volume fraction of secondary carbides increased with the drawing ratio.
• The volume fraction of γ′ decreased as the drawing ratio increased.
• The drawing ratio affected the γ′ volume fraction with no variation of the γ' size.
• The volume fraction of γ′ was affected by the secondary carbide volume fraction.

Inconel X-750 is a Ni-based precipitation-hardened superalloy having large tensile and fracture strengths. In the study, X-750 wires were cold drawn to different extents. Small angle neutron scattering was employed to quantitatively measure the size and volume fraction of the γ′ phase as a function of the cold drawing ratio (DR) and aging temperature. The presence and size of γ′ precipitates were confirmed by transmission electron microscopy. The drawing ratio had an important effect on the volume fraction of the γ′ precipitates. However, the size of the precipitates was independent on the drawing ratio. The specimen with the minimum drawing ratio (DR0) produced the largest volume fraction of γ′ as compared with large drawing ratio (DR) specimens such as DR17 and DR42. The small volume fraction of the γ′ phase for a sizeable drawing ratio was associated with the large amount of nucleation sites for secondary carbides, M23C6, and the fast diffusion path, i.e., dislocation, needed to form M23C6. A Cr depletion zone around the secondary carbides raised the solubility of γ′. Therefore, the significant drawing ratio contributing to the large volume fraction of the secondary carbides decreased the volume fraction of the γ′ precipitates in Inconel X-750.