Morphology and composition of Ni–Co electrodeposited powders

The morphology, phase and chemical composition of Ni–Co alloy powders electrodeposited from an ammonium sulfate-boric acid containing electrolyte with different ratio of Ni/Co ions were investigated. The ratios of Ni/Co ions were 1/1, 1/2 and 1/3. The morphology, chemical composition and phase composition of the electrodeposited alloy powders were investigated using AES, SEM, EDS and XRD analysis. Composition of the electrolyte, i.e. the ratio of Ni/Co concentrations was found to influence both, the alloy phase composition and the morphology of Ni–Co alloy powders. At the highest ratio of Ni/Co = 1/1 concentrations typical 2D fern-like dendritic particles were obtained. With a decrease of Ni/Co ions ratio among 2D fern-like dendrites, 3D dendrites and different agglomerates were obtained. X-ray diffraction studies showed that the alloy powders mainly consisted of the face-centered cubic α-nickel phase and hexagonal close-packed ε-cobalt phase and minor proportions of face-centered cubic α-cobalt phase. The occurrence of the latter phase was observed only in the alloy powder with the higher cobalt concentration in electrolyte. The electrodeposition of Ni–Co powders occurred in an anomalous manner.

► Ni-Co alloys powders were successfully electrodeposited.
► Composition of the electrolyte (Ni/Co ions ratio) was found to influence on morphology of powders.
► The electrodeposition of Ni–Co powders occurred in an anomalous manner.