![عکس صفحه اول مقاله: Enhancement effect of inter-pass annealing during equal channel angular pressing on grain refinement and ductility of 9Cr1Mo steel Enhancement effect of inter-pass annealing during equal channel angular pressing on grain refinement and ductility of 9Cr1Mo steel](/preview/png/1573331.png)
To obtain enhanced mechanical property in both the strength and the ductility, 9Cr1Mo steel (T91) was severely deformed by equal channel angular pressing (ECAP) combined with an additional inter-pass annealing. Tensile results show that the additional inter-pass annealing can significantly improve the ductility (i.e. 18% of the total elongation after four-pass extrusion with the inter-pass annealing) but slightly decrease the tensile strength comparing with the case without the inter-pass annealing (i.e. 10% of the total elongation after four-pass ECAP processing). The average grain size of the two passes ECAP-processed materials with the inter-pass annealing (~0.8 µm) is smaller than that of the sample without inter-pass annealing (~2 µm), and the fraction of the high angle grain boundaries in the samples with the inter-pass annealing (~40%) is higher than that of ~34% (two-pass ECAP) without the inter-pass annealing based on electron backscattering diffraction analysis. The crystallite size and dislocation density were evaluated by means of the modified Williamson-Hall plot based on X-ray diffraction analysis. The microstructural analysis indicates that the enhanced ductility of the ECAP processed and inter-pass annealed materials can be attributed to the relatively smaller grain sizes, larger crystallite sizes and lower dislocation densities.
Journal: Materials Science and Engineering: A - Volume 667, 14 June 2016, Pages 454–458