On the synergy of diffusible hydrogen content and hydrogen diffusivity in the mechanical degradation of laboratory cast Fe-C alloys
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: On the synergy of diffusible hydrogen content and hydrogen diffusivity in the mechanical degradation of laboratory cast Fe-C alloys On the synergy of diffusible hydrogen content and hydrogen diffusivity in the mechanical degradation of laboratory cast Fe-C alloys](/preview/png/1573418.png)
چکیده انگلیسی
The present work investigates the influence of hydrogen on the mechanical properties of generic Fe-C alloys by tensile tests on notched samples. Different microstructures, such as pearlite, bainite and martensite are generated in a 0.2%C Fe-C alloy by an appropriate heat treatment. “Pure” iron is used as a reference material and a variation in the carbon content up to 0.4% is established for the bainitic grade. The effect of hydrogen is demonstrated by mechanical tests on both in-situ hydrogen charged and uncharged specimens. At high cross-head deformation speed (5Â mm/min), the results indicate a considerable, though variable hydrogen effect for different microstructures. The bainitic and martensitic materials both show ductility drops of about 20%, whereas the pearlitic and ferritic grades display a higher sensitivity to hydrogen embrittlement (HE) with a ductility loss of approximately 50%. In order to evaluate the role of the diffusible hydrogen, tensile tests are performed at a lower cross-head deformation speed (0.05Â mm/min) as well. Next to the correlation between the amount of diffusible hydrogen and HE, the distance over which hydrogen can diffuse during a tensile test, determined by hydrogen diffusion coefficient, seems to play a crucial role as well.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 664, 10 May 2016, Pages 195-205
Journal: Materials Science and Engineering: A - Volume 664, 10 May 2016, Pages 195-205
نویسندگان
T. Depover, E. Wallaert, K. Verbeken,