Deformation behavior of an extruded Mg-Dy-Zn alloy with long period stacking ordered phase
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Deformation behavior of an extruded Mg-2Dy-0.5Zn (at%) alloy was investigated under uniaxial tensile test at a range of strain rates of 3Ã10â5-3Ã10â1 sâ1 and temperature ranging from room temperature (RT) to 300 °C. The microstructure of the alloy was mainly composed of α-Mg, (Mg, Zn)xDy particle phase and a large number of long period stacking ordered (LPSO) phases. The tensile testing results indicated that strain rate sensitivity exponent (m) generally increased with increasing temperature and decreasing strain rate. Interestingly, m exhibited two different values in logÏâlogÎµÌ curves at 300 °C, indicating that the plastic deformation mechanism of the alloy occurred to change. The surface and microstructure observations of the tensile specimens after tension revealed that the deformation behavior of the alloy was similar to that of the metal matrix composites, where the load transferred from the Mg matrix to the LPSO phase at low temperatures (RT~200 °C) under different strain rates and at 300 °C under high strain rates, while the grain boundary sliding accommodated by dislocation slip dominated the whole deformation behavior at 300 °C under low strain rates. The alloy exhibited a quasi-superplastic deformation with an elongation-to-failure of 105% at 300 °C and 3Ã10â5 sâ1. The quasi-superplastic deformation was attributed to the stable grains retained by the precipitation of the LPSO phase with good thermal stability in grain interior at an elevated temperature.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 622, 12 January 2015, Pages 52-60
Journal: Materials Science and Engineering: A - Volume 622, 12 January 2015, Pages 52-60
نویسندگان
Guangli Bi, Yuandong Li, Xiaofeng Huang, Tijun Chen, Jianshe Lian, Zhonghao Jiang, Ying Ma, Yuan Hao,