Effect of austenite deformation in non-recrystallization region on microstructure development in low-silicon content TRIP-assisted steels
ترجمه فارسی عنوان
تأثیر تغییر شکل آستنیت در منطقه عدم غلظت بازیابی بر رشد ریزساختار در محیط کم سیلیکون
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
چکیده انگلیسی
The influence of austenite deformation in non-recrystallization region on microstructural development in low-silicon content TRIP-assisted steels was investigated. Laboratory simulation of a typical thermomechanical control processing was carried out in an automated hot-compression testing machine. Specimens subjected to a typical multi-stage isothermal deformation/cooling program were deformed to true strains of 0, â0.15, â0.25 and â0.35 at various temperatures in austenite non-recrystallization region. Mössbauer spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM) and a novel tint-etching method were used to investigate the microstructure of deformed specimens. The results indicated that the maximum volume fraction (VRA) and carbon content (CRA%) of retained austenite can be obtained by deforming samples to some intermediate strains (ε=â0.15 for VRA and ε=â0.25 for CRA%). However, further straining of samples to ε=â0.35 resulted in a drastic reduction of both parameters due to formation of pearlite. It was found that a decrease in deformation temperature resulted in increasing VRA and CRA%. Moreover, deformation of austenite was associated with morphology changes in retained austenite particles from interlath film-like type in undeformed specimens to blocky and encapsulated types in the deformed specimens.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 618, 17 November 2014, Pages 63-70
Journal: Materials Science and Engineering: A - Volume 618, 17 November 2014, Pages 63-70
نویسندگان
Seyed Mohammad Kazem Hosseini, Abbass Zaeri-Hanzaki, Steve Yue,