Enhanced work hardening by redistribution of oxygen in (α+β)-type Ti-4Cr-0.2O alloys
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Enhanced work hardening by redistribution of oxygen in (α+β)-type Ti-4Cr-0.2O alloys Enhanced work hardening by redistribution of oxygen in (α+β)-type Ti-4Cr-0.2O alloys](/preview/png/1575038.png)
چکیده انگلیسی
Tensile deformation behavior of an (α+β) dual-phase Ti-4%Cr alloy containing 0.2% oxygen was compared to that of a low-oxygen Ti-4%Cr alloy. The effect of oxygen content on work hardening behavior is discussed herein in terms of inhomogeneous deformation, which relates to the strength ratio of the α and β phases. In the low-oxygen Ti-4%Cr alloy, plastic deformation preferentially occurred in the α phase because the hardness of the β phase is significantly higher. On the other hand, in the Ti-4%Cr-0.2%O alloy, not only the α phase but also the β phase deformed plastically during tensile deformation owing to their similar hardness, where oxygen concentrated into the α phase and increased the hardness by solid solution strengthening. As a result of plastic deformation of the β phase, {332}<113>β deformation twins were formed within the β grains and caused a significant work hardening due to twinning-induced plasticity (TWIP). This leads to good ductility of the Ti-4%Cr-0.2%O alloy in spite of its higher strength compared to the Ti-4%Cr alloy.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 606, 12 June 2014, Pages 101-107
Journal: Materials Science and Engineering: A - Volume 606, 12 June 2014, Pages 101-107
نویسندگان
Duck-Soo Kang, Norimitsu Koga, Masayuki Sakata, Nobuo Nakada, Toshihiro Tsuchiyama, Setsuo Takaki,