Phase transformations and mechanical properties in heat treated superaustenitic stainless steels

A microstructure-properties relationship study in two superaustenitic stainless steels (S31254 and S32654) was carried out, following exposure at elevated temperatures for various ageing times. Due to high temperature ageing, most stainless steel grades suffer the formation of various precipitates, directly affecting their properties. The full characterization of those precipitates and the correlation with the mechanical behavior of the steels is the primary aim of this study. Samples of the steel grades studied, were exposed to isothermal heat treatments within the temperature range of 650-950 °C, for ageing times varying between 0.5 h and 3000 h, followed by water quenching at room temperature. Microstructural examination indicated the formation of four different secondary phases, sigma phase (σ), chi phase (χ), Laves phase and β-Cr2N nitride, which were characterized by transmission electron microscopy (TEM) and electron diffraction. The results obtained permitted the construction of the time-temperature-precipitation (TTP) plots. In addition, tensile and Vickers hardness testing were utilized and the modulus of toughness was calculated. The kinetics of the formation of various precipitates with increasing temperature and aging duration was also observed. It was found that various precipitates had a significant effect on all mechanical properties studied.