کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
1576593 | 1514781 | 2013 | 8 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
The effect of heat treatment on recrystallized microstructure, precipitation and ductility of hot-rolled Fe-Cr-Al-REM ferritic stainless steel sheets
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: The effect of heat treatment on recrystallized microstructure, precipitation and ductility of hot-rolled Fe-Cr-Al-REM ferritic stainless steel sheets The effect of heat treatment on recrystallized microstructure, precipitation and ductility of hot-rolled Fe-Cr-Al-REM ferritic stainless steel sheets](/preview/png/1576593.png)
چکیده انگلیسی
This study presents research works about the effects of heat treatment on recrystallized equiaxed grain size, precipitation, room temperature (RT) toughness and ductile to brittle transition temperature (DBTT) of Fe-Cr-Al-REM ferritic stainless steel (FSS) hot-rolled sheet. Results showed that the recrystallization of hot-rolled Fe-Cr-Al-REM FSS sheet could be completed after annealing treatment at 750 °C for 15 min with the equiaxed grain diameter of approximately 50 μm. Inappropriate annealing treatment would inevitably leads to the unexpected grain coarsening. On the other hand, a great deal of needle-like or spot-like fine aluminum-lanthanum compound Al11La3 precipitates were observed in the ferrite matrix after 1 h aging treatment at 750 °C. The microstructure observation results associated with the impact test definitely illustrated that the Al11La3 precipitates was the reason for the brittle crack in the as-casted ingot and as-forged slab. The real DBTT of the annealed Fe-Cr-Al-REM FSS sheet with average grain size of about 50 μm was â4 °C. Meanwhile, the DBTT of the hot-rolled Fe-Cr-Al-REM stainless steel sheet was evidently increased as the recrystallized grain size increased.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 562, 1 February 2013, Pages 9-16
Journal: Materials Science and Engineering: A - Volume 562, 1 February 2013, Pages 9-16
نویسندگان
H.P. Qu, Y.P. Lang, C.F. Yao, H.T. Chen, C.Q. Yang,