The present work deals with the microstructure evolution of a pure copper processed by a new severe plastic deformation method. A set of pure copper (99.99%) work-pieces with coarse-grained microstructures was processed by accumulative back extrusion (ABE) method at room temperature. The optical and scanning electron microscopy (SEM) and hardness measurements were utilized to study the microstructural evolution and hardness homogeneity. The results indicated that ABE is a capable process to provide a homogenous grain refined microstructure in pure copper. The observed grain refinement was discussed relying on the occurrence of dynamic restoration processes. The analysis of microstructure and hardness showed outstanding homogeneity improvement throughout the work-pieces as the consecutive ABE passes were applied. The homogeneity improvement was attributed to the propagation of the shear bands and also the heavily deformed regions. A reversing route was also applied in the ABE processing to investigate its effect on the development of microstructural homogeneity. Comparing to the conventional route, the application of the reversing route was found to yield better homogeneity after less passes of the process.
Journal: Materials Science and Engineering: A - Volume 559, 1 January 2013, Pages 595–600