The tensile behaviors of polycrystalline Ni-base superalloys have been studied in the temperature range of 25–980 °C. Anomalous increase of yield strength was observed in precipitation hardened superalloys at intermediate temperature. The alloy with high γ′ volume fraction showed a remarkable increase of yield strength at intermediate temperature. A peak of yield strength was observed in the alloy with low γ′ volume fraction at intermediate temperature while solid solution strengthened alloys did not have such peak. Abrupt decrease of ductility in the intermediate temperature regime was observed not only in the γ′ strengthened superalloys but also in the solid solution strengthened superalloy. This result implies that γ′ precipitation is not a substantial cause for the occurrence of the ductility minimum in the superalloys. It was found that twinning was an important deformation mechanism of the superalloys at intermediate temperature where ductility was abnormally low. Deformation twins formed easily in the superalloys whose reduction of stacking fault energy was high regardless of strengthening mechanisms because alloys with low stacking fault energy was prone to extend stacking faults.
► Abrupt decrease of elongation in the intermediate temperatures is found in the superalloys.
► Microtwinning is a predominant deformation mechanism at intermediate temperature where the ductility minimum occurs.
► Deformation twins tend to form in the superalloys whose reduction of stacking fault energy is high.
Journal: Materials Science and Engineering: A - Volume 528, Issue 24, 15 September 2011, Pages 7149–7155