Ultrahigh strength and low yield ratio of niobium-microalloyed 900Â MPa pipeline steel with nano/ultrafine bainitic lath

An ultra-low carbon niobium-microalloyed steel with yield strength of ∼900 MPa has been processed on a pilot-plant scale. The microstructure of the steel is primarily characterized by lower bainite and acicular ferrite, with small fraction of lath-martensite and martensite-austenite (MA) constituents. Bainite is present as fine domains. A combination of niobium and titanium precipitates was observed at the grain boundaries and in the interior of the grains and includes irregular (∼40-150 nm of (Nb, Ti)(C, N)) and fine cuboidal/spherical particles of NbC (∼30-50 nm). It was observed that accelerated cooling inhibited the precipitation of Nb and Ti carbides. The Charpy impact toughness at −20 °C was 200 J and tensile elongation was 15% with the yield ratio of less than 0.84. The good matching of high strength and low yield ratio was realized by two-stage thermo-mechanical rolling combined with fast cooling.