عنوان انگلیسی مقاله ISI
Active brazing carbon/carbon composite to TC4 with Cu and Mo composite interlayers
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Active brazing carbon/carbon composite to TC4 with Cu and Mo composite interlayers Active brazing carbon/carbon composite to TC4 with Cu and Mo composite interlayers](/preview/png/1579793.png)
چکیده انگلیسی
Active filler metal (TiZrNiCu) was used to increase the wettability and Cu and Mo composite interlayers were added to release residual stress and increase the mechanical properties of TC4-C/C composite joints. The mechanical properties of the brazed joints were measured by shear strength testing. The effects of brazing parameters on the microstructures of the brazed joint were investigated by SEM, EDS and XRD. It is shown that the maximum shear strength of the joints is 21 MPa brazed at 900 °C for 5 min, which is about 3 times greater than brazing alloy alone. When the brazing temperature is low, the interface structure of C/C composite/Cu brazed joint is Cu/Cu51Zr14/Ti2(Cu,Ni) + Ti(Cu,Ni) + TiCu + Cu2TiZr/(Ti,Zr)C/C/C composite. With the increased brazing temperature, Ti2(Cu,Ni), Ti(Cu,Ni), TiCu and Cu2TiZr reaction phases disappear. Cu(s.s) and Ti(Cu,Ni)2 appear. The thicknesses of Cu51Zr14 and (Ti,Zr)C reaction layers increase. When the brazing temperature is high, the interface structure change to Cu/Cu51Zr14/Cu(s.s) + Ti(Cu,Ni)2/(Ti,Zr)C/C/C composite.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 525, Issues 1â2, 15 November 2009, Pages 181-185
Journal: Materials Science and Engineering: A - Volume 525, Issues 1â2, 15 November 2009, Pages 181-185
نویسندگان
Youqiong Qin, Jicai Feng,