Nano-grained 70/30 brass strip produced by accumulative roll-bonding (ARB) process
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Nano-grained 70/30 brass strip produced by accumulative roll-bonding (ARB) process Nano-grained 70/30 brass strip produced by accumulative roll-bonding (ARB) process](/preview/png/1579918.png)
چکیده انگلیسی
Accumulative roll-bonding process is the only severe plastic deformation (SPD) process using rolling deformation itself, and has been used for 70/30 brass up to 6 cycles at ambient temperature under unlubricated conditions. Microstructural characterizations were done by transmission electron microscopy (TEM). After 6 cycles it was found that continuous recrystallization occurred and the microstructure covered with small recrystallized grains with an average diameter below 100Â nm. The tensile tests and Vickers macro- and microhardness were conducted on the ARBed 70/30 brass. A scanning electron microscopy (SEM) study was performed in order to observe the shear bands and also to clarify the failure mechanism. The tensile strength and hardness became two and three times greater than the initial value respectively. However, the elongation dropped abruptly at the first cycle, then increased slightly. Strengthening in ARBed 70/30 brass explained by strain hardening in the first step and grain refinement at high strains. Observations revealed that the failure mode in ARBed 70/30 brass was a shearing ductile rupture with elongated shallow shear dimples.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 527, Issue 3, 15 January 2010, Pages 491-497
Journal: Materials Science and Engineering: A - Volume 527, Issue 3, 15 January 2010, Pages 491-497
نویسندگان
Somayeh Pasebani, Mohammad Reza Toroghinejad,