Study of SiO2/PMMA/CE tri-component interpenetrating polymer network composites

A technology of conjugated tri-component interpenetrating polymer networks was applied to synthesize a nano-SiO2/polymethylmethacrylate (PMMA)/cyanate (CE) composite through an asynchronous synthesis way. The microstructure of the composite was characterized using infrared spectroscopy (IR) and transmission electron microscopy (TEM). The mechanical properties were measured in German-made DL-1000B and XCL-40 universal material test machines, respectively. Results showed that both the impact strength and the flexural strength were in the optimum status when 3% SiO2/PMMA/CE was chosen as a sample with the PMMA/CE ratio of 20/80. Compared with the strengths of pure cyanate, those of the composite were raised by 137.28% and 31.29%, respectively. When 3% nano-SiO2 was added, the impact strength was increased by 29.96% and the flexural strength by 20.05%, compared with the strengths of polymers without SiO2. Analysis and measurements by IR and TEM indicated that no chemical reactions took place among components in the composite. The interpenetration of the conjugated tri-component improved the loading capacity of the polymer, hence the toughness enhancement of cyanate.