Hot compressive deformation behavior and microstructure evolution of Ti-6Al-2Zr-1Mo-1V alloy at 1073Â K

Hot compressive behaviors of Ti-6Al-2Zr-1Mo-1V alloy at 1073 K, as well as the evolution of microstructure during deformation process, were investigated in this paper. The results shows that flow stress increases up to a peak stress, then decease with increasing strain, and forms a stable stage at last. The grain size also shows an decrease at first and increase after a minimum value. Dislocations are observed to produce at the interface of α/β phase, and the phase interface and dislocation circle play an important role in impeding the movement of dislocation. As strain increase, micro-deformation bands with high-density dislocation are founded, and dynamic recrystallization occurs.