The pure elemental powder mixtures with the compositions of Mg65NixSi35−x (x = 10, 20, 25, 33 at.%) were subject to high-energy ball mill, and the structures of the mixtures at different intervals of milling were characterised by X-ray diffraction (XRD). The compositional dependency of the glass forming ability (GFA) in Mg–Ni–Si system was evaluated based on the experimental results and the theoretical calculation. The compositional dependency of GFA in Mg–Ni–Si system can be understood well by comparing the enthalpies of the crystalline and amorphous phases based on the Miedema's theory for the formation enthalpy of alloys. Increasing the Ni/Mg ratio and/or decreasing Si content can improve the amorphous formability. The calculation results might be of great help in optimising the composition with high GFA in Mg–Ni–Si system.
Journal: Materials Science and Engineering: A - Volume 459, Issues 1–2, 25 June 2007, Pages 35–39