Magnetic and magnetocaloric properties of Pr0.6−xEuxSr0.4MnO3 manganese oxides

Studies of the structural, magnetic and magnetocaloric properties of polycrystalline Pr0.6−xEuxSr0.4MnO3 (0≤x≤0.15) perovskite manganites were carried out. Substitution for praseodymium with europium, with smaller ionic radius, induces local distortion in the 〈Mn–O–Mn〉 bonds and consequently causes a random distribution in the magnetic exchange interactions. The competition between magnetic interactions leads to the appearance of an inhomogeneous magnetic state in our samples. Pr0.6−xEuxSr0.4MnO3 (x=0x=0, 0.05, 0.1 and 0.15) polycrystalline samples were prepared using the solid–solid reaction method at high temperature. The compounds yielded are single phase and crystallize in the orthorhombic system with the Pnma space group. The substitution of Eu for Pr leads to a decrease of the Curie temperature TCTC from 303 K for x=0.00x=0.00 to 260 K for x=0.15x=0.15. All of our compounds exhibit a large magnetic entropy change with a maximum around 2.2 J/kg K under a magnetic applied field change of 2 T for all compounds.

► The effect of Eu substitution in Pr0.6−xEuxSr0.4MnO3 is studied.
► The Curie temperature TCTC decreases from 303 K (x=0.0x=0.0) to 260 K (x=0.15x=0.15).
► There is a maximum magnetic entropy change of 2.2 J/kg K under a 2 T change.