The amorphization tendency of a B2 phase in Ti50Ni50−xFex (x = 2 to 40 at%) intermetallic compound was investigated in order to determine the relationship between solid-state amorphization (SSA) and martensite transformation. SSA was observed in the B2 phase at 103 K and 298 K by high-voltage electron microscopy (HVEM). The total dose required for the amorphization increased with the Fe content. The replacement of Ni by Fe increased the phase stability of the B2 phase in Ti–Ni–Fe intermetallic compound and suppressed SSA as well as martensite transformation.
Figure optionsDownload as PowerPoint slideHighlights
► The relationship between solid-state amorphization and martensite transformation was investigated.
► The amorphization tendency of a B2 phase in Ti50Ni50−xFex (x = 2 to 40 at%) was clarified.
► Solid-state amorphization was observed in the B2 phase at 103 K and 298 K by HVEM.
► The total dose required for the amorphization increased with the Fe content.
► The replacement of Ni by Fe suppressed SSA as well as martensite transformation.
Journal: Intermetallics - Volume 19, Issue 9, September 2011, Pages 1313–1318