Phase equilibria in the Al–Si–V system: The vanadium rich part

The V-rich part of the Al–Si–V phase diagram was determined by a combination of optical microscopy, powder X-ray diffraction (XRD), differential thermal analysis (DTA) and electron probe microanalysis (EPMA). Phase equilibria were investigated at two isothermal sections at 850 and 1300 °C. High temperature DTA was performed to identify the ternary invariant reactions yielding a ternary reaction scheme and the vertical section at 50 at.% V. As cast samples were investigated in order to gain additional information about primary crystallization fields. A liquidus surface projection was constructed for the entire ternary system by combining our experimental data with those from literature.

Figure optionsDownload as PowerPoint slideResearch highlights
► Isothermal sections at 850 and 1300 °C in Al–Si–V.
► Complete liquidus surface projection.
► High temperature phase equilibria in the V-rich part.