A study on the surface severe plastic deformation behavior of a Zr-based bulk metallic glass (BMG)
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: A study on the surface severe plastic deformation behavior of a Zr-based bulk metallic glass (BMG) A study on the surface severe plastic deformation behavior of a Zr-based bulk metallic glass (BMG)](/preview/png/1601561.png)
چکیده انگلیسی
A surface treatment process, which can generate the severe plastic deformation in the near-surface layer of crystalline materials, is successfully applied on the Zr50Cu40Al10 bulk metallic glass (BMG). The experiment is implemented using 20 WC/Co balls with a velocity of about 5Â m/s to bombard the surface of the samples in a purified argon atmosphere. The plastic-flow deformation in the unconstrained sample edge was observed, which exhibits the good intrinsic ductility of this material under the experimental condition. In the sub-surface layer, the bombardment-induced shear-band operations generate the extrusion and intrusion marks on the side face. Differential scanning calorimetry (DSC) shows that the free volumes of the deformed BMG have increased, and possible crystallization may occur during the process. X-ray diffraction (XRD) and synchrotron high-energy X-ray diffraction techniques were used to inspect the possible crystal phase. A nanoindentation test shows that on the side surface, the hardness increases and, then, decreases with the distance from the processed surface. Four-point-bending-fatigue behavior has been studied and related to the modified surface structure and the compressive residual stress introduced by the surface treatment.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Intermetallics - Volume 17, Issue 11, November 2009, Pages 951-957
Journal: Intermetallics - Volume 17, Issue 11, November 2009, Pages 951-957
نویسندگان
J.W. Tian, L.L. Shaw, Y.D. Wang, Y. Yokoyama, P.K. Liaw,