Evolution of crystallographic texture in the orthorhombic phase of a two-phase alloy Ti–22Al–25Nb (at%), consisting of orthorhombic (O) and bcc (β/B2) phases, was studied. The material was subjected to deformation in two-phase field as well as in the single β phase field. The resulting evolution of microstructure and crystallographic texture were recorded using scanning electron microscopy and X-ray diffraction. The orthorhombic phase underwent change in morphology (from platelets to equiaxed) on rolling in the two-phase field with the texture getting sharper with the amount of deformation. Rolling above β transus temperature led to hot deformation of single β phase microstructure and its subsequent cooling produced transformed coarse platelets of orthorhombic phase with texture in orientation relation with the high temperature deformed β phase.
Journal: Intermetallics - Volume 17, Issue 8, August 2009, Pages 622–633