Precipitation of Cr-rich phases in rapidly solidified Ni-20Al-8Cr (at.%) powders

The segregation of chromium and boron in the form of borides removes these elements from the intermetallic matrix, so the content of both elements should be optimised to preserve their beneficial influence on the ductility of the γ′-Ni3Al phase.