Low Cycle Fatigue Behavior and Cyclic Softening of P92 Ferritic-martensitic Steel
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Low Cycle Fatigue Behavior and Cyclic Softening of P92 Ferritic-martensitic Steel Low Cycle Fatigue Behavior and Cyclic Softening of P92 Ferritic-martensitic Steel](/preview/png/1628277.png)
چکیده انگلیسی
The low cycle fatigue (LCF) behavior of P92 martensitic steel was investigated under different controlled strain amplitudes at room and high temperatures (873 K). The cyclic stress responses at all temperatures and strain amplitudes exhibited obviously rapid softening behavior at the early stage of fatigue life, and there was no saturated stage at high temperature. The fracture surfaces of the fatigue samples were observed by scanning electron microscopy (SEM) and optical microscopy. It was shown that crack initiation and propagation occurred transgranularly at both testing temperatures. A typical character was the high density crack branches or secondary cracks along fatigue striations at high temperature, which initiated from the oxidized inclusions and grain boundaries. Further investigation by transmission electron microscopy (TEM) showed that the softening behavior was attributed to the microstructure evolution during fatigue life, such as annihilation of dislocations and migration of martensite laths as well as carbide coarsening, especially for samples tested at high temperature.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Iron and Steel Research, International - Volume 22, Issue 6, June 2015, Pages 534-542
Journal: Journal of Iron and Steel Research, International - Volume 22, Issue 6, June 2015, Pages 534-542
نویسندگان
Zhen ZHANG, Zheng-fei HU, Li-kun FAN, Bin WANG,