Effect of Ball Scribing on Magnetic Shielding Efficiency of Grain-oriented Silicon Steel

Magnetic shielding of grain-oriented silicon steel was investigated. Ball scribing with spacing of 2 to 16 mm was performed at peak flux densities of 8.0 mT to 1.3 T. Magnetic shielding efficiency was calculated, including absorption, reflection and inner multi-reflection shielding efficiencies. Magnetic shielding efficiency (MSE) increase ratios after different scribing spacing were compared, and thickness requirement to achieve absorption shielding of 50 dB was also calculated. The results show that magnetic shielding efficiencies of C711 and H668 silicon steels increase by 4.79 and 3.15 dB respectively after scribing of 16 mm. Before scribing, shielding efficiency of H668 steel was higher than that of C711 steel, while after scribing, both absorption and shielding efficiency gaps were largely abridged between C711 and H668 steels. Plate thickness of C711 steel could be reduced from 3.18 mm without scribing to 2.20 mm after scribing of 16 mm. There is no apparent thickness reduction at lower flux densities; while the peak flux density is above 0.3 T, the shielding effect becomes apparent, and the thickness could be reduced from 2.28 mm without scribing to 1.70 mm with scribing spacing of 16 mm. Magnetizing process and its effect on variation of magnetic shielding were also analyzed.