Verification of Interpretation of Dynamic Strain Aging for Intermediate Temperature Embrittlement in Ni-Bi Alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Intermediate temperature embrittlement (ITE) is a general phenomenon in Ni alloys and recently was interpreted by dynamic strain aging (DSA). The relationship between ITE and DSA was studied by a binary Ni-Bi alloy. The experimental alloy of well-controlled purity was produced by vacuum induction melting and then heat-treated properly. Tensile tests were performed at various tensile temperatures, and the elongation at fracture was used to indicate the ductility. In order to identify the mechanisms of fracture and ITE, fracture morphologies of the samples of low ductility were observed by scanning electron microscopy. According to the tensile ductility, Ni-Bi alloy shows an obvious embrittlement behavior in the intermediate temperature range (700 - 750 °C). However, the stress-strain curves of Ni-Bi alloy and the fracture morphologies indicate that DSA does not exist over the whole temperature range. Based on the experimental results and literatures, the interpretation of DSA was then discussed and proved to be invalid for elucidating the general feature of ITE in Ni-Bi alloy and Ni-based superalloys.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Iron and Steel Research, International - Volume 22, Issue 7, July 2015, Pages 602-606
Journal: Journal of Iron and Steel Research, International - Volume 22, Issue 7, July 2015, Pages 602-606
نویسندگان
Wu-qiang YANG, Min XU, Ye MENG, Lei ZHENG, Xiao-dong MENG,