Properties of hydrogen permeation barrier on the surface of zirconium hydride

A hydrogen permeation barrier was manufactured by the in situ reaction of zirconium hydride with oxygen. A reduction in the hydrogen permeation of the oxide films was detected by measuring the mass difference of the zirconium hydride samples after the dehydrogenation experiment. The reaction of zirconium hydride with oxygen occurs only under the condition that the temperature is higher than 673 K in the oxygen partial pressure of 0.1 MPa. The oxide film is composed of two layers, a permeable oxide layer and a dense oxide layer, and the main phase of the oxide film is ZrO2 with baddeleyite structure. The XPS analysis shows that O-H bonds exist in the oxide film, which are helpful for resisting hydrogen diffusion through the oxide film.