Fracture characteristics of notched investment cast TiAl alloy through in situ SEM observation
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
TiAl alloys were produced by investment casting method combined with induction skull melting (ISM) technique. In situ scanning electron microscopy (SEM) was utilized to study the fracture characteristics and crack propagation of a notched investment cast TiAl specimens in tension under incremental loading conditions. The whole process of crack initiation, propagation and failure during tensile deformation was observed and characterized. The results show that the fracture mechanism was sensitive to not only the microcracks near the notched area but also lamellar orientation to loading axis. The high tensile stress leads to the new microcracks nucleate along lamellar interfaces of grains with favorable orientation when local stress intensity reaches the toughness threshold of the material. Thus, both plasticity and high tensile stress are required to cause notched TiAl failure.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Transactions of Nonferrous Metals Society of China - Volume 22, Issue 10, October 2012, Pages 2389-2394
Journal: Transactions of Nonferrous Metals Society of China - Volume 22, Issue 10, October 2012, Pages 2389-2394
نویسندگان
Yan-fei CHEN, Shun-qi ZHENG, Jiang-ping TU, Shu-long XIAO, Jing TIAN, Li-juan XU, Yu-yong CHEN,