Preparation, Structure Characterization and Hydrodesulfurization Performance of B-Ni2P/SBA-15/Cordierite Monolithic Catalysts

A series of B-Ni2P/SBA-15/cord monolithic catalysts were prepared by coating the slurry of the B-Ni2P/SBA-15 precursors on a pretreated cordierite support, and followed by temperature-programmed reduction in a H2 flow. The samples were characterized by X-ray diffraction (XRD) and N2 adsorption–desorption technique. The catalytic activities for the hydrodesulfurization (HDS) of dibenzothiophene (DBT) were evaluated. The results showed that Ni2P phase was present in all B-Ni2P/SBA-15/cord monolithic catalysts. The specific surface areas (SBET) of the B-Ni2P/SBA-15/cord monolithic catalysts was first increased to 167 m2·g− 1, and then decreased to 155 m2·g− 1 with the increase of boron contents. The catalytic activity also showed the similar trend with the increase of boron contents. The 1.75% (by mass) B-Ni2P/SBA-15/cord monolithic catalysts exhibited the highest DBT conversion of 98.4% at 380 °C. The cordierite-based monolithic catalysts showed better low temperature sensitivity for HDS of DBT in comparison with the particle catalysts. Moreover, two HDS routes, direct desulfurization (DDS) and hydrogenation (HYD), proceeded independently over B-Ni2P/SBA-15/cord monolithic catalysts and the main pathway was DDS.

A series of B-Ni2P/SBA-15/cord monolithic catalysts with different B contents were prepared by coating the slurry of the B-Ni2P/SBA-15 precursors on a pretreated cordierite support, and followed by temperature-programmed reduction in a H2 flow. The structure of monolithic catalysts was characterized and the catalytic activities for the hydrodesulfurization (HDS) of dibenzothiophene (DBT) were evaluated. The cordierite-based monolithic catalysts exhibited the better catalytic activities and low temperature sensitivity for HDS of DBT. Two HDS routes, direct desulfurization (DDS) and hydrogenation (HYD), proceeded independently in the cordierite-based monolithic catalysts and the main pathway was DDS.Figure optionsDownload as PowerPoint slide