Rheological study of polypropylene irradiated with polyfunctional monomers

The aim of this paper is to investigate the rheological properties of polypropylene (PP) modified by ionization radiation (gamma rays) in the presence of two different monomers. The samples were mixed in a twin-screw extruder with ethylene glycol dimethacrylate (EGDMA) or trimethylolpropane trimethacrylate (TMPTMA) with concentration in the range of 0.5–5.0 mmol. After that, they were irradiated with 20 kGy dose of gamma radiation. The structural modification of polypropylene was analyzed in the melt state by measuring melt flow rate (MFR), η* (complex viscosity) and G′ (storage modulus) in the angular frequency range of 10−1 to 3 × 102 rad s−1. From the oscillatory rheology data, one could obtain the values of η0 (zero shear viscosity) that would be related to the molar mass. All results were discussed with respect to the crosslinking and degradation process that occur in the post-reactor treatment to produce controlled rheology polypropylene.The resulting polymeric materials were submitted the cytotoxicity in vitro test by neutral red uptake methodology with NCTC L 929 cell line from American Type Culture Collection bank. All modified PP samples presented no cytotoxicity.