To study the suitability of using graphite as material for high-power targets for rare isotope production at the future Facility for Rare Isotope Beams (FRIB) in the USA and at the Facility for Antiproton and Ion Research (FAIR) in Germany, thin foils of polycrystalline graphite were exposed to 8.6-MeV/u Au ions reaching a maximum fluence of 1 × 1015 ions/cm2. Foil irradiation temperatures of up to 1800 °C were obtained by ohmic heating. In-situ monitoring of the electrical resistance of the graphite foils during and after irradiation provided information on beam-induced radiation damage.The rate of electrical resistance increase as a function of fluence was found to decrease with increasing irradiation temperature, indicating a more efficient annealing of the irradiation-produced defects. This is corroborated by the observation that graphite foils irradiated at temperatures below about 800 °C showed cracks and pronounced deformations, which did not appear on the samples irradiated at higher temperatures.
Journal: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms - Volume 314, 1 November 2013, Pages 125–129