Implantation of Cr-ions in Fe70Co30 thin film have been performed to modify its structural and magnetic properties. From the XRD results, the lattice constant as well as the grain size of the film is increasing with the ion fluence. Cr-ions (1 × 1017 ions/cm2) reduces the coercivity of the film from 140(3) Oe to 44(3) Oe. Coercivity of the film follows the exponential decay as a function of Cr-ions fluence. 35 keV (projectile range 13.5 nm) and 100 keV Cr-ions (projectile range 34.3 nm) have been used to understand the effects of magnetic Cr-ions and the effects of ballistic collision cascade on the MOKE signal. Similar changes on the coercivity behaviour of the film implanted with these two energies have been observed. It appears that the implantation process creates a solid solution of Cr in FeCo without any other additional treatment in the film. After 5 × 1016 Cr-ions, film exhibit four fold magnetic anisotropy.
Journal: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms - Volume 266, Issue 8, April 2008, Pages 1407–1410