![عکس صفحه اول مقاله: Deposition and characterization of smooth ultra-nanocrystalline diamond film in CH4/H2/Ar by microwave plasma chemical vapor deposition Deposition and characterization of smooth ultra-nanocrystalline diamond film in CH4/H2/Ar by microwave plasma chemical vapor deposition](/preview/png/1689022.png)
The smooth ultra-nanocrystalline diamond (UNCD) films were prepared by microwave plasma chemical vapor deposition (MWCVD) using argon-rich CH4/H2/Ar plasmas with varying argon concentration from 96% to 98% and negative bias voltage from 0 to −150 V. The influences of argon concentration and negative bias voltage on the microstructure, morphology and phase composition of the deposited UNCD films are investigated by using scanning electron microscopy (SEM), X-ray diffraction (XRD), atom force microscopy (AFM), and visible and UV Raman spectroscopy. It was found that the introduction of argon in the plasma caused the grain size and surface roughness decrease. The RMS surface roughness of 9.6 nm (10 micron square area) and grain size of about 5.7 nm of smooth UNCD films were achieved on Si(100) substrate. Detailed experimental results and mechanisms for UNCD film deposition in argon-based plasma are discussed. The deposited highly smooth UNCD film is also expected to be applicable in medical implants, surface acoustic wave (SAW) devices and micro-electromechanical systems (MEMS).
Journal: Vacuum - Volume 84, Issue 11, 4 June 2010, Pages 1347–1352